UL
1061/CSA
AWM Semi-Rigid Hook-up Wire
Figure：
1.Conductor：
Annealed Copper Wire，(Bare Single,Tinned
Single, Tinned Strand,or Top-Tinned Strand)
2.Insulation： SR-PVC (Semi-Rigid
Polyvinyl Chloride)
3.Structure：
|
Conductor
|
Insulation
|
Conductor
Resistance(20℃)
|
|
AWG
|
Construction
|
Diameter
|
Min
Thickness
|
Nominal
Thickness
|
Diameter
|
|
30
|
7 / 0.10TA
|
approx.0.30 mm
|
0.229 mm
|
0.25 mm
|
0.80 ±
0.10
mm
|
354.32W
/
Km
|
|
28
|
7 / 0.13TA
|
approx.0.39 mm
|
0.255 mm
|
0.90 ±
0.10
mm
|
223.75W
/
Km
|
|
26
|
7 / 0.16TA
|
approx.0.48 mm
|
0.245 mm
|
0.97 ±
0.10 mm
|
139.76W
/
Km
|
|
24
|
7 / 0.20TA
|
approx.0.60 mm
|
0.425 mm
|
1.10 ±
0.10 mm
|
85.95W
/
Km
|
|
24
|
11 / 0.16TA
|
approx.0.61 mm
|
0.245 mm
|
1.10 ±
0.10 mm
|
85.49W
/
Km
|
|
22
|
7 / 0.26TA
|
approx.0.78 mm
|
0.26 mm
|
1.30 ±
0.10 mm
|
54.79W
/
Km
|
|
22
|
17 / 0.16TA
|
approx.0.76 mm
|
0.27 mm
|
1.30 ±
0.10 mm
|
59.74W
/
Km
|
|
20
|
7 / 0.32TA
|
approx.0.96 mm
|
0.27 mm
|
1.50 ±
0.10 mm
|
34.12W
/
Km
|
|
20
|
21 / 0.18TA
|
approx.0.95 mm
|
0.275 mm
|
1.50 ±
0.10 mm
|
38.46W
/
Km
|
|
18
|
34 / 0.18TA
|
approx.1.21 mm
|
0.245 mm
|
1.70 ±
0.10 mm
|
24.70W
/
Km
|
|
18
|
42 / 0.16TA
|
approx.1.20 mm
|
0.25 mm
|
1.70 ±
0.10 mm
|
25.34W
/
Km
|
|
30
|
1 / 0.26TA
|
approx.0.26 mm
|
0.27 mm
|
0.80 ±
0.10 mm
|
359W
/
Km
|
|
28
|
1 / 0.32TA
|
approx.0.32 mm
|
0.265 mm
|
0.85 ±
0.10 mm
|
232W
/
Km
|
|
26
|
1 / 041TA
|
approx.0.41 mm
|
0.27 mm
|
0.95 ± 0.10 mm
|
146W / Km
|
|
24
|
1 / 0.51TA
|
approx.0.51 mm
|
0.27 mm
|
1.05 ± 0.10 mm
|
89.20W / Km
|
|
22
|
1 / 0.65TA
|
approx.0.65 mm
|
0.275 mm
|
1.20 ± 0.10 mm
|
56.30W / Km
|
|
20
|
1 / 0.813TA
|
approx.0.813 mm
|
0.268 mm
|
1.35 ±
0.10 mm
|
35.20W
/
Km
|
4.Characteristics：
|
Items
|
Specification
|
|
Rating
|
UL：80℃
300V ，
CSA：80℃
300V
|
|
Dielectric Strength
|
AC 1000V / min.
|
|
Insulation Resistance
|
Min. 5MW
- Km (20℃)
at DC 500V
|
|
Flame Test
|
UL：VW-1 CSA：FT-1
|
|
Elongation of Insulation
|
Min.100 ﹪
|
|
Tensile Strength of Insulation
|
Min.2.11Kg / mm2
|
|
Residual of Elongation after Aging
|
Min.
65 ﹪of
original (113℃，168H)
|
|
Residual of Tensile Strength after Aging
|
Min.
70 ﹪of
original (113℃，168H)
|
5.Marking：E54979
AWM 1061 80℃
300V
VW – 1 □AWG
TATUNG
LL58500 CSA
AWM I A 80 | 